COATINO®

Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Mill base

Pos.	Component	Amount	Producer
1	SILIKOPON® EF	11 g
2	TEGO® Airex 900	22 g
3	AEROSIL® R 972	33 g
4	KRONOS 2360	44 g
5	BLANC FIXE Brilliant	55 g	Solvay S.A.
6	Butyl acetate	66 g
	Total	70.5 g

SILIKOPON® EF

11 g

TEGO® Airex 900

22 g

AEROSIL® R 972

33 g

KRONOS 2360

44 g

BLANC FIXE Brilliant

55 g

Solvay S.A.

Butyl acetate

66 g

Preparation

Weigh in

SILIKOPON® EF

Add components 2 to 6 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Step 2

Let Down

Pos.	Component	Amount	Producer
7	SILIKOPON® EF	77 g
8	ALBIDUR® 1223	88 g
9	TEGO® Wet 270	99 g
10	TINUVIN® 292	110 g	BASF SE
11	Butyl acetate	121 g
	Total	100.0 g

SILIKOPON® EF

77 g

ALBIDUR® 1223

88 g

TEGO® Wet 270

99 g

TINUVIN® 292

110 g

BASF SE

Butyl acetate

121 g

Preparation

Add components 7 to 11 while stirring.

Properties

Attribute	Conditions	Value	unit
Theoretical solids content		approx. 95	%
Cup efflux time	Cup: DIN 6	35 - 45	s
Density		1.45	g/cm³
VOC-Content		approx. 65	g/l

Theoretical solids content

approx. 95 %

Cup efflux time

35 - 45 s

Conditions: Cup: DIN 6

Density

1.45 g/cm³

VOC-Content

approx. 65 g/l

Attribute	Conditions	Value	unit
Dry to touch (tack-free)	23 °C	8.5	h
Dry trough	23 °C	> 10	d
Full cure	23 °C	14	d
Wet film thickness		95 - 130	µm
Dry film thickness		60 - 80	µm

Attribute

Conditions

Value

unit

Dry to touch (tack-free)

23 °C

8.5

Dry trough

23 °C

> 10

Full cure

23 °C

Wet film thickness

95 - 130

µm

Dry film thickness

60 - 80

µm

2K topcoat based on SILIKOPON® EF, white

Login

Preparation

Mill base

Preparation

Let Down

Preparation

Properties

Formulations variants

Mixing ratio

Application

Example - High pressure spraying