1K topcoat based on SILIKOPHEN® AC 1000, white

Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Mill base

Pos.	Component	Amount	Producer
1	SILIKOPHEN® AC 1000	11 g
2	BENTONE® SD-2	22 g	Elementis
3	AEROSIL® R 972	33 g
4	KRONOS 2190	44 g
	Total	73.1 g

SILIKOPHEN® AC 1000

11 g

BENTONE® SD-2

22 g

Elementis

AEROSIL® R 972

33 g

KRONOS 2190

44 g

Preparation

Weigh in

SILIKOPHEN® AC 1000

Add components 2 to 4 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Step 2

Let Down

Pos.	Component	Amount	Producer
5	SILIKOPHEN® AC 1000	55 g
6	ALBIDUR® 1223	66 g
7	TINUVIN® 292	77 g	BASF SE
8	TINUVIN® 400	88 g	BASF SE
9	TEGO® Glide 100	99 g
	Total	100.0 g

SILIKOPHEN® AC 1000

55 g

ALBIDUR® 1223

66 g

TINUVIN® 292

77 g

BASF SE

TINUVIN® 400

88 g

BASF SE

TEGO® Glide 100

99 g

Preparation

Add components 6 to 9 while stirring.

Properties

Attribute	Conditions	Value	unit
Theoretical solids content		approx. 71	%
Cup efflux time	Cup: DIN 5	18 - 28	s
Density		1.56	g/cm³

Theoretical solids content

approx. 71 %

Cup efflux time

18 - 28 s

Conditions: Cup: DIN 5

Density

1.56 g/cm³

Attribute	Conditions	Value	unit
Dry trough	approx. 23 °C & 50% rH	2 - 3	h
Wet film thickness		60 - 80	µm
Dry film thickness		25 - 40	µm

Attribute

Conditions

Value

unit

Dry trough

approx. 23 °C & 50% rH

2 - 3

Wet film thickness

60 - 80

µm

Dry film thickness

25 - 40

µm

1K topcoat based on SILIKOPHEN® AC 1000, white

Login

Preparation

Mill base

Preparation

Let Down

Preparation

Properties

Formulations variants

Mixing ratio

Application

Example - High pressure spraying