Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Mill base

Pos.	Component	Amount	Producer
1	SILIKOPHEN® AC 1000	11 g
2	Xylene	22 g
3	TEGO® Dispers 628	33 g
4	TEGO® Wet 270	44 g
5	BENTONE® SD-1	55 g	Elementis
6	MICA TM	66 g	Aspanger Bergbau und Mineralwerke GmbH & Co KG
7	HEUCOPHOS® ZPO	77 g
8	HEUCODUR® Black 9-100	88 g
9	AEROSIL® R 972	99 g
	Total	88.7 g

SILIKOPHEN® AC 1000

11 g

Xylene

22 g

TEGO® Dispers 628

33 g

TEGO® Wet 270

44 g

BENTONE® SD-1

55 g

Elementis

MICA TM

66 g

Aspanger Bergbau und Mineralwerke GmbH & Co KG

HEUCOPHOS® ZPO

77 g

HEUCODUR® Black 9-100

88 g

AEROSIL® R 972

99 g

Preparation

Weigh in

SILIKOPHEN® AC 1000

Add components 2 to 9 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Step 2

Let Down

Pos.	Component	Amount
10	Butyl glycol acetate	110 g
11	Xylene	121 g
	Total	100.0 g

Preparation

Add components 10 to 11 while stirring.

Properties

Attribute	Conditions	Value	unit
Theoretical solids content		approx. 70	%
Cup efflux time	Cup: DIN 4	18 - 28	s
Density		1.34	g/cm³
VOC-Content		approx. 393	g/l

Theoretical solids content

approx. 70 %

Cup efflux time

18 - 28 s

Conditions: Cup: DIN 4

Density

1.34 g/cm³

VOC-Content

approx. 393 g/l

Attribute	Conditions	Value	unit
Dry trough	approx. 23 °C & 50% rH	2 - 3	h
Wet film thickness		50 - 60	µm
Dry film thickness		20 - 25	µm

1K high heat-resistant coating based on SILIKOPHEN® AC 1000, black

Login

Preparation

Mill base

Preparation

Let Down

Preparation

Properties

Formulations variants

Application

Example - High pressure spraying