COATINO®

Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Mill base

Pos.	Component	Amount	Producer
1	SILIKOTOP® E 901	11 g
2	TEGO® Airex 922	22 g
3	TEGO® Dispers 628	33 g
4	BENTONE® SD-2	44 g	Elementis
5	SYLOSIV® A3	55 g	W.R. Grace & Co.
6	AEROSIL® R 972	66 g
7	Microtalc IT Extra	77 g	Elementis
8	HEUCOPHOS® CAPP	88 g
9	KRONOS 2360	99 g
10	BLANC FIXE micro	110 g	Solvay S.A.
11	ShellSol® D60	121 g	Shell Chemicals
12	Butyl acetate	132 g
	Total	66.5 g

SILIKOTOP® E 901

11 g

TEGO® Airex 922

22 g

TEGO® Dispers 628

33 g

BENTONE® SD-2

44 g

Elementis

SYLOSIV® A3

55 g

W.R. Grace & Co.

AEROSIL® R 972

66 g

Microtalc IT Extra

77 g

Elementis

HEUCOPHOS® CAPP

88 g

KRONOS 2360

99 g

BLANC FIXE micro

110 g

Solvay S.A.

ShellSol® D60

121 g

Shell Chemicals

Butyl acetate

132 g

Preparation

Weigh in

SILIKOTOP® E 901

Add components 2 to 12 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Step 2

Let Down

Pos.	Component	Amount	Producer
13	SILIKOTOP® E 901	143 g
14	Mixture: 1.0% TIB KAT® 218 99.0% Butyl acetate	154 g	TIB Chemicals AG
15	TINUVIN® 292	165 g	BASF SE
16	TINUVIN® 400	176 g	BASF SE
17	Butyl acetate	187 g
18	Butyl acetate	198 g
	Total	100.0 g

SILIKOTOP® E 901

143 g

Mixture:

1.0% TIB KAT® 218

99.0% Butyl acetate

154 g

TINUVIN® 292

165 g

BASF SE

TINUVIN® 400

176 g

BASF SE

Butyl acetate

187 g

Butyl acetate

198 g

Preparation

Add components 13 to 17 while stirring.

Adjust to application viscosity by adding component 18.

Properties

Attribute	Conditions	Value	unit
Theoretical solids content		approx. 80	%
Cup efflux time	Cup: DIN 4	40 - 50	s
Density		1.43	g/cm³
VOC-Content		approx. 300	g/l

Theoretical solids content

approx. 80 %

Cup efflux time

40 - 50 s

Conditions: Cup: DIN 4

Density

1.43 g/cm³

VOC-Content

approx. 300 g/l

Formulations variants

Mixing ratio

Coating

100.0 g

VESTANAT® HT 2500 LV

25.7 g

Properties

Attribute	Conditions	Value	unit
Pot life	23°C	approx. 30	min
VOC-Content		approx. 225	g/l

Pot life

approx. 30 min

Conditions: 23°C

VOC-Content

approx. 225 g/l

Application

Attribute	Conditions	Value	unit
Dry to touch (tack-free)	23 °C	5	h
Dry trough	23 °C	12	h
Full cure	23 °C	14	d
Wet film thickness		85 - 110	µm
Dry film thickness		60 - 80	µm

Dry to touch (tack-free)

5 h

Conditions: 23 °C

Dry trough

12 h

Conditions: 23 °C

Full cure

14 d

Conditions: 23 °C

Wet film thickness

85 - 110 µm

Dry film thickness

60 - 80 µm

Example - High pressure spraying

Model: SATAjet® 4000 B RP

Nozzle size: 1.4 mm

Pressure: 2 bar

2K high solids topcoat based on SILIKOTOP® E 901, white

Login

Preparation

Mill base

Preparation

Let Down

Preparation

Properties

Formulations variants

Mixing ratio

Properties

Application

Example - High pressure spraying