COATINO®

Preparation

Select the desired amount for the preparation step.

Planned amount

Step 1

Mill base

Pos.	Component	Amount	Producer
1	SILIKOPHEN® P 80/X	11 g
2	TEGO® Wet 270	22 g
3	TEGO® Airex 900	33 g
4	Isobutanol	44 g
5	Xylene	55 g
6	BLANC FIXE N	66 g	Solvay S.A.
7	AEROSIL® R 972	77 g
	Total	69.9 g

SILIKOPHEN® P 80/X

11 g

TEGO® Wet 270

22 g

TEGO® Airex 900

33 g

Isobutanol

44 g

Xylene

55 g

BLANC FIXE N

66 g

Solvay S.A.

AEROSIL® R 972

77 g

Preparation

Weigh in

SILIKOPHEN® P 80/X

Add components 2 to 7 while stirring.

Dispers in the bead mill until the required particle size is reached (< 20 µm).

Step 2

Let Down

Pos.	Component	Amount	Producer
8	STAPA® 4 n.l.	88 g	Eckart GmbH
9	Xylene	99 g
	Total	100.0 g

Preparation

Add component 8 while stirring.

Adjust to application viscosity by adding component 9.

Properties

Attribute	Value	unit
Theoretical solids content	approx. 64	%
Density	1.24	g/cm³
VOC-Content	approx. 450	g/l

Theoretical solids content

approx. 64 %

Density

1.24 g/cm³

VOC-Content

approx. 450 g/l

Attribute	Conditions	Value	unit
Flash-off time	23 °C	30	min
Curing condition	250 °C	30	min
Wet film thickness		50 - 65	µm
Dry film thickness		20 - 25	µm

Attribute

Conditions

Value

unit

Flash-off time

23 °C

min

Curing condition

250 °C

min

Wet film thickness

50 - 65

µm

Dry film thickness

20 - 25

µm

SILIKOPHEN® P 80/X color: aluminum

Login

Preparation

Mill base

Preparation

Let Down

Preparation

Properties

Formulations variants

Application

Example - High pressure spraying