Silicone hybrid

1K high heat-resistant coating based on SILIKOFTAL® HTF MPA/MBA, white

1K high heat-resistant coating based on SILIKOFTAL HTF MPA/MBA® E 901, heatstable up to 250°C / 482°F , high solids, FDA 175.300 complain, white

Type

Silicone hybrid

Color

White

Pigments

KRONOS 2190 - PW 6

Key products

SILIKOFTAL® HTF MPA/MBA

Markets

Technologies

Solventborne

Created by

Paint bucket representation of 1K high heat-resistant coating based on SILIKOFTAL® HTF MPA/MBA, white

Login

Please login with your account to see all formulation details.

Preparation

Select the desired amount for the preparation step.

Step 1

Mill base

1
SILIKOFTAL® HTF MPA/MBA
11 g
company logo
2
KRONOS 2190
22 g
company logo
3
AEROSIL® R 972
33 g
company logo

Preparation

Weigh in SILIKOFTAL® HTF MPA/MBA
.
Add components 2 to 3 while stirring.
Dispers in the bead mill until the required particle size is reached (< 20 µm).
Step 2

Let Down

4
SILIKOFTAL® HTF MPA/MBA
44 g
company logo
5

1-Methoxy-2-propyl acetate

55 g
6

Butyl acetate

66 g

Preparation

Add components 4 to 6 while stirring.

Properties

Theoretical solids content
approx. 67 %
Cup efflux time
30 - 40 s
Conditions: Cup: DIN 4

Formulations variants

Application

Flash-off time
30 min
Conditions: 23 °C
Curing condition
30 min
Conditions: 250 °C
Wet film thickness
85 - 110 µm
Dry film thickness
60 - 80 µm

Example - High pressure spraying

Model: SATAjet® 4000 B RP
Nozzle size: 1.4 mm
Pressure: 2 bar